Zirconia ceramic gears have very good wear resistance, higher wear resistance than cemented carbide, and have the advantages of corrosion resistance, non-magnetic conduction and non-conduction that cemented carbide does not have, self-lubricating, and environmental protection.
It will not oxidize under certain high temperature environment. Our zirconia ceramic gear can achieve no color spots on the surface and no visible pores. Zirconia not only has the advantages of high hardness, high wear resistance, high temperature resistance, etc., it does not oxidize under certain high temperature environment.
It is also a very tough material in fine ceramics, so it is often used in structural parts and wear-resistant parts. In addition to being commonly used in the field of industrial structural parts, zirconium oxide has a jade-like texture and is widely used in living ceramics.
Custom Zirconia Ceramic Components in different shapes and different colors :
Zirconia Ceramic Tube Rod Pin Shaft
ZrO2 Zirconia Ceramic ring, flange
Zirconia Bezel watch ring
Zirconia plunger, piston
ZrO2 Zirconia ceramic washer, wafer
spacerZirconia Ceramic Substrate Sheet
Zirconia ceramic bladeZirconia ceramic plate
Zirconia blockZro2 Zirconia ceramic tube, bushing , Sleeve, bush
Zirconia Ceramic BallZirconia valve , valve seat
Zirconia Components for sand milling machine
Zirconia Ceramic Dispersing Disk , Zirconia Disc
Zirconia Cone for wire guide , Zirconia ceramic roller pulley
Zirconia grinding head
| XY Ceramic Property | ||||||||
|---|---|---|---|---|---|---|---|---|
| Type | Unit | Zirconium | ||||||
| XY Grade | Z-100 | Z-200 | Z-300 | ZM-100 | ZB-100 | |||
| Material | ZrO2-Y2O3 | ZrO2-Y2O3 | ZrO2-Y2O3 | ZrO2-MgO | ZrO2-Y2O3 | |||
| colour | white | white | white | yellow | blue | |||
| Density | g/cm3 | 6 | 6.03 | 6.04 | 5.62 | 6.03 | ||
| Flexural Strength | Mpa | 900 | 1050 | 1200 | 450 | 1100 | ||
| Compressive Strength | Mpa | 2100 | 2200 | 2300 | 1600 | 2300 | ||
| Modules of Elasticity | Gpa | 200 | 210 | 220 | 210 | 220 | ||
| Fracture Toughness | MPam1/2 | 6 | 7 | 8 | 5.5 | 7 | ||
| Poision's Ratio | 0.3 | 0.3 | 0.3 | 0.3 | 0.3 | |||
| Hardness HRA | HRA | 89 | 90 | 90 | 88 | 90 | ||
| Vickers Hardness | HV1 | 1250 | 1450 | 1450 | 1240 | 1450 | ||
| Thermal Expansion Coefficient | 10-6K-1 | 11 | 10 | 10 | 10 | 10 | ||
| Thermal Conductivity | W/mk | 3 | 3 | 3 | 3 | 3 | ||
| Thermal Shock Resistance | △T.℃ | 400 | 400 | 400 | 400 | |||
| Maximum Use Temperature in Oxidizing Atmosphere | ℃ | 1000 | 1000 | 1000 | 850 | 1000 | ||
| Max Use Temperature in Reducing or Inert Atmosphere | ℃ | 1000 | 1000 | 1000 | 850 | 1000 | ||
| Volume Resistivity at 20℃ （20℃体积电阻） | Ωcm | 10^13 | 10^12 | 10^12 | 5X10^13 | 10^12 | ||
| Dielectric Strength （介电强度） | kV/mm | 19 | 15 | 17 | 19 | 17 |